超薄熔融石英窗鏡

0.20mm 超薄厚度
採用紫外熔融石英基材
重量極輕

TECHSPEC® 超薄熔融石英窗鏡具有熔融石英玻璃的優點，包括熱膨脹率低、耐化學腐蝕性強和紫外波段穿透率高，而厚度卻不到標準熔融石英窗鏡的 1/5。與傳統的保護玻璃不同，這些窗鏡的表面經過拋光處理，可提供一致的穿透波前畸變，因此非常適合 OEM 應用。超薄設計非常適合對重量和尺寸敏感的應用，尤其是需要從紫外到近紅外寬頻傳輸的應用。TECHSPEC 超薄熔融石英窗鏡是掌上型醫療設備、可穿戴技術以及攜帶式紫外燈源的理想選擇。

技術資訊

FUSED SILICA
	Typical transmission of a 3mm thick, uncoated fused silica window across the UV - NIR spectra. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with MgF2 (400-700nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_avg ≤ 1.75% @ 400 - 700nm (N-BK7) Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with UV-AR (250-425nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_abs ≤ 1.0% @ 250 - 425nm R_avg ≤ 0.75% @ 250 - 425nm R_avg ≤ 0.5% @ 370 - 420nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with UV-VIS (250-700nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_abs ≤ 1.0% @ 350 - 450nm R_avg ≤ 1.5% @ 250 - 700nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with VIS-EXT (350-700nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_avg≤ 0.5% @ 350 - 700nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with VIS-NIR (400-1000nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_abs≤ 0.25% @ 880nm R_avg≤ 1.25% @ 400 - 870nm R_avg≤ 1.25% @ 890 - 1000nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with VIS 0° (425-675nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_avg≤ 0.4% @ 425 - 675nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with YAG-BBAR (500-1100nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_abs ≤ 0.25% @ 532nm R_abs ≤ 0.25% @ 1064nm R_avg≤ 1.0% @ 500 - 1100nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with NIR I (600 - 1050nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_avg≤ 0.5% @ 600 - 1050nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data
	Typical transmission of a 3mm thick fused silica window with NIR II (750 - 1550nm) coating at 0° AOI. The blue shaded region indicates the coating design wavelengh range, with the following specification: R_abs ≤ 1.5% @ 750 - 800nm R_abs ≤ 1.0% @ 800 - 1550nm R_avg≤ 0.7% @ 750 - 1550nm Data outside this range is not guaranteed and is for reference only. Click Here to Download Data