Abbe Number (v_d):

67.8

Bevel:

Protective as needed

Clear Aperture (%):

90

Clear Aperture CA (mm):

22.50

Diameter (mm):

25.00 +0.00/-0.10

Thickness (mm):

3.00 ±0.10

Coating:

Uncoated

Coefficient of Thermal Expansion CTE (10^-6/°C):

0.51 (0 to +100°C)
0.58 (0 to +200°C)

Density (g/cm³):

2.20

Edges:

Fine Ground

Index of Refraction n_d:

1.459

Knoop Hardness (kg/mm²):

591

Parallelism (arcsec):

<5

Poisson's Ratio:

0.17

Substrate: Many glass manufacturers offer the same material characteristics under different trade names. Learn More

Suprasil® 300

Surface Quality:

10-5

Transmitted Wavefront, P-V:

λ/10

Type:

Protective Window

Wavelength Range (nm):

200 - 3500

Young's Modulus (GPa):

70

Regulatory Compliance

RoHS:

Compliant

Certificate of Conformance:

View

產品系列說明

在 200 至 3500nm 範圍內具有高穿透效果
1 ppm 以下的 OH 內容物，可盡量減少吸收損耗
10-5 表面品質及最高 λ/10不規則度 TWD

Suprasil® 窗鏡是以高純度的合成熔融石英製造，可在 200 至 3500nm 提供高度及平直的穿透效果。Suprasil 的機械屬性類似於熔融石英，其中的額外優點就是在可見光或紅外線光譜沒有吸收帶，因此在 1400 - 2700nm 之間沒有穿透損耗。相較於 Infrasil®，Suprasil 之中的 OH 內容物低於 1 ppm，因此吸收率較低，在搭配使用高功率雷射時，因為大量吸收造成的溫度上升非常有限，可忽略不計。Suprasil 窗鏡適用於雷射材料加工、醫療雷射應用，或是使用摻釹或 2 微米雷射的應用。

Transmission of Suprasil 300 compared to Corning 7980

25mm Dia., 3mm Thick, Uncoated, Suprasil Window

Regulatory Compliance

產品系列說明